REPSOL ISPLEN PC392AT is a copolymer compound with 30% calcium carbonate and high melt flow rate. It shows good impact strength, medium rigidity, high stiffness, low warpage and low shrinkage behaviour. This product is high heat stabilized. Applications - Technical parts in general Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PC392AV is a copolymer compound with 30% calcium carbonate and high melt flow rate. It shows good impact strength, medium rigidity, high stiffness, low warpage and low shrinkage behaviour. This product is UV stabilized and antistatic formulated. Applications Aesthetic applications which require good gloss surface. - Garden furniture - Toys - Household Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PC470AS is a homopolymer compound with 40% calcium carbonate and high melt flow rate. It shows good impact strength, medium rigidity, high stiffness, low warpage and low shrinkage behaviour. This product is antistatic formulated. Applications Aesthetic applications which require good gloss surface. • Garden furniture • Toys • Household Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PC474AV is a copolymer compound charged with 40% calcium carbonate and high melt flow rate. It shows good impact strength, medium rigidity, high stiffness, low warpage and low shrinkage behavior. It is UV stabilized and antistatic formulated. Applications - Garden furniture - Toys - Household Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PF600R1M is a phthalate free ultra high fluidity random copolymer, intended for the manufacturing of very thin wall articles due to its excellent balance of mechanical properties that allows the manufacturing of flexible, translucent, and consistent pieces with very thin walls. Its antistatic additive package improves demoulding properties providing shorter cycle times and better aesthetic finished such as reduction of the presence of dust and dirt during storage. Applications REPSOL ISPLEN PF600R1M is specially designed for: • Very Thin wall domestic containers • Boxes and crates for domestic and professional storage. • Very thin wall containers and closures for food products: dairy desserts, jams.... Recommended melt temperature range from 230 to 250ºC. Processing conditions should be optimised for each production line.

REPSOL ISPLEN PG180AS is a polypropylene homopolymer, 10% chemically coupled fiber glass reinforced compound. It shows a high stiffness, keeping good impact strength at every range of temperatures. It also shows a low warpage and shrinkage behaviour. Applications - Automotive and structural parts. - Electrical housings, power tools. - Technical pieces in general.

REPSOL ISPLEN PG182AS is a polypropylene copolymer, 10% chemically coupled fiberglass reinforced compound. It shows a high stiffness, keeping good impact strength at every range of temperatures. It also shows a low warpage and shrinkage behavior. Applications • Technical pieces in general. • Automotive and structural parts. • Garden furniture.

REPSOL ISPLEN PG270AS is a reinforced polypropylene compound characterized by a very high stiffness, good impact strength at every range of temperatures, low warpage and low shrinkage behavior. Applications - Technical parts with good surface finish. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PG320AT is a homopolimer reinforced compound. It shows a very high stiffness, with good impact strength at every range of temperatures. It also shows a low warpage and low shrinkage behavior. This product is high heat stabilized. Applications - Automotive: under the bonnet parts subjected to severe mechanical stresses (Light housings, heat and ventilation housings, filters) - Technical parts, in general. - Electrical housings, power tools - Washing machines cylinders Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PG331AS000 is a phthalate free random copolymer 30% chemically-coupled fiber glass reinforced compound. It shows a very high stiffness, with good impact strength at every range of temperatures. It also shows a low warpage and low shrinkage behavior. This product is high heat stabilized. Applications • Specially indicated for the core layer of 3-layer pipes for hot and cold water with pressure. Recommended melt temperature range from 205 to 225ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PG362AV is a polypropylene copolymer, 30% chemically coupled fiber glass reinforced compound. It shows a very high stiffness, keeping good impact strength at every range of temperatures. It also shows a low warpage and shrinkage behaviour. This product is UV stabilized. Applications - Technical pieces, in general Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PG370AS polypropylene homopolymer reinforced compound. It shows a very high stiffness, keeping good impact strength at every range of temperatures. It also shows a low warpage and shrinkage behaviour. Applications • Automotive: under the bonnet parts subjected to severe mechanical stresses • Technical parts, in general. • Electrical housings, power tools. • Garden furniture. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PG370AT polypropylene homopolymer reinforced compound. It shows a very high stiffness, keeping good impact strength at every range of temperatures. It also shows a low warpage and shrinkage behaviour. Applications - Automotive: under the bonnet parts subjected to severe mechanical stresses (Light housings, heat and ventilation housings, filters) - Technical parts, in general. - Electrical housings, power tools - Washing machines cylinders Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

Polypropylene homopolymer, 30% chemically coupled fiber glass reinforced compound. ISPLEN PG370 AV shows a very high stiffness, keeping good impact strength at every range of temperatures. It also shows a low warpage and shrinkage behavior. The product is high heat stabilized and UV protection. Applications - Automotive: Under the bonnet parts subjected to severe mechanical stresses (Light housings, heat and ventilation housings, filters) - Technical pieces, in general. - Electrical housings, power tools. - Washing machines cylinders.

REPSOL ISPLEN PG370BS polypropylene homopolymer, 30% chemically coupled fiber glass reinforced compound. It shows a very high stiffness, keeping good impact strength at every range of temperatures. It also shows a low warpage and shrinkage behaviour. Applications • Automotive: under the bonnet parts subjected to severe mechanical stresses (Light housings, heat and ventilation housings, filters) • Technical parts, in general. • Electrical housings, power tools. • Washing machines cylinders. • Garden furniture. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PG370CS is a polypropylene homopolymer reinforced compound. It shows a very high stiffness, keeping good impact strength at every range of temperatures. It also shows a low warpage and shrinkage behavior. This product is standard stabilized. Applications • Automotive: under the bonnet parts subjected to severe mechanical stresses (Light housings, heat and ventilation housings, filters) • Technical parts, in general. • Electrical housings, power tools • Washing machines cylinders. • Garden furniture. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PG370CT is a polypropylene homopolymer reinforced compound. It shows a very high stiffness, keeping good impact strength at every range of temperatures. It also shows a low warpage and shrinkage behavior. This product is high heat stabilized. Applications - Automotive: under the bonnet parts subjected to severe mechanical stresses (Light housings, heat and ventilation housings, filters) - Technical parts, in general. - Electrical housings, power tools - Washing machines cylinders. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PG370CV polypropylene homopolymer reinforced compound. It shows a very high stiffness, keeping good impact strength at every range of temperatures. This product is UV and high heat stabilized. Applications • Automotive: under the bonnet parts subjected to severe mechanical stresses • Technical parts, in general. • Garden furniture. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PG370ES polypropylene homopolymer reinforced compound. It shows a very high stiffness, keeping good impact strength at every range of temperatures. It also shows a low warpage and shrinkage behavior. Applications - Automotive: Under the bonnet parts subjected to severe mechanical stresses. - Electrical housings, power tools. - Technical pieces, in general. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PG470AT polypropylene homopolymer, 40% chemically coupled fiber glass reinforced compound. It shows a very high stiffness, keeping good impact strength. It also shows a low warpage and shrinkage behaviour. Applications • Automotive: under the bonnet parts subjected to severe mechanical stresses (Light housings, heat and ventilation housings, filters) • Technical parts, in general. • Electrical housings, power tools • Washing machines cylinders Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line

REPSOL ISPLEN PG560AV polypropylene homopolymer, 50% chemically coupled fiberglass-reinforced compound. It shows a very high stiffness, keeping good impact strength at every range of temperatures. It also shows a low warpage and shrinkage behavior. This material is thermal, and UV stabilized. Applications - Automotive: parts subjected to severe mechanical stresses - Technical parts, in general. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

Polypropylene copolymer, 20% mineral fillers reinforced and good melt flow rate. ISPLEN PM281 EV was designed showing a high stiffness with a good impact resistance, and a low warpage and high shrinkage behaviour. It shows really good gloss surface and an excellent scratch resistance. The product is UV stabilised. APPLICATIONS Automotive: - Interior trims and panels. - Technical pieces, in general.

Polypropylene homopolymer, 30% mineral fillers reinforced and high melt flow rate. ISPLEN PM370 AV gives a good compromise between stiffness and impact strength, a low warpage and shrinkage behaviour. This product is high heat stabilised. APPLICATIONS - Automotive: Under the bonnet parts subjected to high thermal stress (Light housings, heat and ventilation ducts), air conditioning elements inside the car - White goods: components in washing machines. - Technical pieces, in general.

REPSOL ISPLEN PM162AV is a copolymer compound with 10% mineral filler reinforced and high melt flow rate. It shows good impact strength, medium rigidity, high stiffness, low warpage and low shrinkage behaviour. This product is UV stabilized. Applications - Automotive: Interior trims and panels - Technical parts, in general. - Electrical appliances Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PM170AS polypropylene homopolymer, 10% mineral fillers reinforced and good melt flow rate. It was designed showing a high stiffness with a good impact resistance, and a low warpage and shrinkage behaviour. Applications - Technical parts, in general. - Electrical appliances. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PM181AS is a copolymer compound with 10% mineral filler reinforced and high melt flow rate. It shows good balance between impact strength and stiffness. Applications • Automotive: Interior trims and panels • Technical parts, in general. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PM220AS is a polypropylene homopolymer, 20% mineral fillers reinforced and medium melt flow rate. It a high stiffness, as well as a low warpage and shrinkage behaviour. Applications • Automotive: Under the bonnet parts • Technical parts: profiles • Air conditioning elements inside the car Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PM240AS is a polypropylene homopolymer, 20% mineral fillers reinforced and low melt flow rate. It gives a high stiffness, and a low warpage and shrinkage behaviour. Applications • Automotive: parts under the hood, subject to the action of temperature (headlight housings, ventilation and heating elements) • Air conditioning elements inside the car • Home appliances: power tool casings • Technical pieces, in general Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PM240AT is a polypropylene homopolymer, 20% mineral fillers reinforced and low melt flow rate. It gives a high stiffness, and a low warpage and shrinkage behaviour. The product is high heat stabilized. Applications Automotive: • Under the bonnet parts subjected to high thermal stress (Light housings, heat and ventilation ducts). • Air conditioning elements inside the car • Home appliances: power tool casings • Technical pieces, in general Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PM250DX is a polypropylene homopolymer, 20% mineral fillers reinforced and medium melt flow rate. It shows an improved high stiffness, as well as a low warpage and shrinkage behaviour. The product is high heat stabilized specially designed for being in contact with detergents. Applications - Washing machines cylinders and others electrical appliances in contact with detergents. - Technical pieces, in general. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PM252AS is a polypropylene copolymer, 20% mineral fillers reinforced and good melt flow rate. It gives a high impact even at low temperatures showing a good stiffness, as well as a low warpage and shrinkage behaviour. Applications • Automotive: Under the bonnet parts subjected to high thermal stress (Light housings, heat and ventilation ducts). • Heaters and air conditioning units. • Technical pieces, in general. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PM270AT is a polypropylene homopolymer, 20% mineral fillers reinforced and high melt flow rate. It gives a high stiffness, and a low warpage and shrinkage behaviour. This product is high heat stabilized. Applications - Automotive: Under the bonnet parts subjected to high thermal stress (Light housings, heat and ventilation ducts). - Heaters and air conditioning units. - Technical pieces, in general. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PM270DT is a polypropylene homopolymer, 20% mineral fillers reinforced and high melt flow rate. It gives a high stiffness, and a low warpage and shrinkage behaviour. This product is high heat and UV stabilized. Applications • Automotive: Under the bonnet parts subjected to high thermal stress (Light housings, heat and ventilation ducts). • Heater and air conditioning units • Technical pieces, in general. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PM270RT is a polypropylene homopolymer, 20% mineral fillers reinforced and high melt flow rate. It gives a high stiffness, and a low warpage and shrinkage behaviour. This product is high heat stabilized and it shows low emission and low odor properties. Applications - Automotive: Under the bonnet parts subjected to high thermal stress (Light housings, heat and ventilation ducts). - Heaters and air conditioning units. - Technical pieces, in general. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PM274AS is a polypropylene copolymer, 20% mineral fillers reinforced and with high processability. It shows high stiffness and good impact strength. It gives good aesthetic properties and high gloss surface. The product has a standard stabilization, able to be used in the main applications. Applications - Automotive: insertion, steps, structural parts - Electrical appliances and white line. - Technical pieces, in general. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PM274AT is a polypropylene copolymer, 20% mineral fillers reinforced and with high processability. It shows a good compromise between impact strength and stiffness, keeping a low warpage and shrinkage behaviour. The product is high heat stabilized. Applications • Automotive: Under the bonnet parts subjected to high thermal stress. Interior trims. • Technical pieces, in general. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PM274AV is a polypropylene copolymer, 20% mineral fillers reinforced and with high processability. It shows high stiffness and good impact strength. It gives good aesthetic properties and high gloss surface. The product is UV stabilized. Applications - Automotive. - Technical pieces, in general. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PM274BV is a polypropylene copolymer, 20% mineral fillers reinforced and with high processability. It shows a good compromise between impact strength and stiffness, keeping a low warpage and shrinkage behaviour. The product is high UV and heat stabilized. Applications • Technical pieces, in general. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PM276FV is a copolymer 17% mineral fillers reinforced. It shows good stiffness/impact resistance balance and demoulding properties during the transformation process. The product is UV stabilized. Applications - Automotive: Interior trims and panels. - Technical pieces, in general. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.

REPSOL ISPLEN PM276JV is a copolymer 16% mineral fillers reinforced. It shows a high impact resistance with a good scratch resistance, and good stiffness and demoulding properties during the transformation process. The product is UV stabilized. Applications - Automotive: Interior trims and panels. - Technical pieces, in general. Recommended melt temperature range from 190 to 250ºC. Processing conditions should be optimized for each production line.