Celanex® 2300 GV3/20
20% glass bead reinforced, lubricated and stabilized lower warpage grade
Chemical abbreviation according to ISO 1043-1: PBT Moulding compound ISO 7792- PBT, MGHR, 08-040N, GB20 Polybutylene terephthalate, low warpage, 20 % glass beads. Flammability UL 94 HB minimum thickness 0.82 mm. Recognition by Underwriters Laboratories, USA (UL)
Chemical abbreviation according to ISO 1043-1: PBT Moulding compound ISO 7792- PBT, MGHR, 08-040N, GB20 Polybutylene terephthalate, low warpage, 20 % glass beads. Flammability UL 94 HB minimum thickness 0.82 mm. Recognition by Underwriters Laboratories, USA (UL)
一般属性
使用 Prospector 建立免費帳戶時，可造訪 Celanex® 2300 GV3/20 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊
物料形态
已商用：当前有效
文档
可用性
北美洲, 非洲和中东, 拉丁美洲, 欧洲, 亚太地区
用途
汽车领域的应用
汽车规格
CONTINENTAL SN 57908-17
加工方式
注射成型
多点数据
- Isothermal Stress vs. Strain (ISO 11403)
- Secant Modulus vs. Strain (ISO 11403)
- Shear Modulus vs. Temperature, Dynamic (ISO 11403)
- Shear Stress vs. Shear Rate (ISO 11403)
- Viscosity vs. Shear Rate (ISO 11403)
其他属性
填料/增强材料, 添加剂, 特性, 形式, 密度, 熔融体积流量（MVR）, 收缩率, 吸水率Sat/23C, 吸水率23C/50RH, 粘数, 拉伸模量, 拉伸断裂应力, 拉伸断裂应变, 拉伸蠕变模量 (1h), 拉伸蠕变模量 (1000h), 弯曲应力, 简支梁缺口冲击强度, 简支梁无缺口冲击强度, 球压硬度, DTUL (0.45 MPa) 未退火, DTUL (1.80 MPa) 未退火, 维卡软化温度, 熔融温度, 线性热膨胀系数，流动, 表面电阻率, 体积电阻率, 介电强度, 相对电容率, 耗散因数, 相比耐漏电起痕指数(CTI), UL 阻燃等级, 极限氧指数, 其他性能, 干燥温度, 干燥时间, 建议的最大水分含量, 料斗温度, 料筒后部温度, 料筒中部温度, 料筒前部温度, 射嘴温度, 加工（熔体）温度, 模具温度, 注射速度
加工
Find specific processing information for Celanex® PBT as well as general information for the 聚丁烯对苯二甲酸酯 generic family. 注册 或 登录 了解更多信息。