VESTAMID® L LX9012 T8
VESTAMID® LX9012 T8 has been especially developed for the extrusion and co-extrusion of ski upper and decorative films. Decoration on the bottom side of injection molded sports shoe soles is a further application field.
Films made of VESTAMID® LX9012 T8 feature high transparency, good screen and sublimation printing, outstanding scratch resistance, and excellent impact strength at low temperatures. The semi-crystalline compounds based on PA 12 absorb only low quantities of water.
Therefore, molded parts show excellent dimensional stability, constantly high impact strength, low coefficient of friction and good chemical resistance at changing ambient humidity.
Films made of VESTAMID® LX9012 T8 feature high transparency, good screen and sublimation printing, outstanding scratch resistance, and excellent impact strength at low temperatures. The semi-crystalline compounds based on PA 12 absorb only low quantities of water.
Therefore, molded parts show excellent dimensional stability, constantly high impact strength, low coefficient of friction and good chemical resistance at changing ambient humidity.
一般属性
使用 Prospector 建立免費帳戶時，可造訪 VESTAMID® L LX9012 T8 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊
物料形态
已商用：当前有效
可用性
北美洲, 欧洲
用途
体育用品
加工方式
薄膜挤出
其他属性
添加剂, 特性, 外观, 形式, 密度 / 比重, 密度, 熔融体积流量（MVR）, 收缩率, 吸水率Sat/23C, 吸水率23C/50RH, 拉伸模量, 拉伸屈服应力, 拉伸断裂应力, 拉伸应力, 拉伸屈服应变, 标称拉伸断裂应变, 弯曲模量, 弯曲应力, 简支梁缺口冲击强度, 简支梁无缺口冲击强度, 肖氏硬度, 肖氏硬度, DTUL (0.45 MPa) 未退火, DTUL (1.80 MPa) 未退火, 玻璃转化温度, 维卡软化温度, 熔融峰值温度, 熔融温度, 线性热膨胀系数，流动, 体积电阻率, 介电强度, 相对电容率, 耗散因数, 可燃性等级, 其他性能, 加工（熔体）温度, 模具温度
加工
Find specific processing information for VESTAMID® L Polyamide 12 as well as general information for the 聚酰胺 12 generic family. 注册 或 登录 了解更多信息。