VESTAMID® L L1930 NC
VESTAMID® L1930 NC is a heat stabilized, with 30% milled glass fiber-reinforced PA 12 compound suitable for injection molding of stiff, relatively warp free molded parts.
Due to the reinforcement moldings from this compound exhibit a high strength and rigidity. Because PA 12 absorbs only little water, the parts have a good dimensional stability and almost unaffected mechanical properties at changing ambient humidity.
Due to the reinforcement the shrinking of moldings is decreased compared with unreinforced compounds. Using specialty short glass fibers for the reinforcement of VESTAMID® L1930 NC the difference between longitudinal and transverse shrinkage relating to the flow direction of the melt is significantly lower than with common glass fiber-reinforced products. Therefore especially low-warpage precision parts can be molded.
As a semi-crystalline material VESTAMID® L1930 NC feature an outstanding chemical resistance, e.g., against fuels, oils and fats.
Pigmentation may affect values.
Due to the reinforcement moldings from this compound exhibit a high strength and rigidity. Because PA 12 absorbs only little water, the parts have a good dimensional stability and almost unaffected mechanical properties at changing ambient humidity.
Due to the reinforcement the shrinking of moldings is decreased compared with unreinforced compounds. Using specialty short glass fibers for the reinforcement of VESTAMID® L1930 NC the difference between longitudinal and transverse shrinkage relating to the flow direction of the melt is significantly lower than with common glass fiber-reinforced products. Therefore especially low-warpage precision parts can be molded.
As a semi-crystalline material VESTAMID® L1930 NC feature an outstanding chemical resistance, e.g., against fuels, oils and fats.
Pigmentation may affect values.
一般属性
使用 Prospector 建立免費帳戶時，可造訪 VESTAMID® L L1930 NC 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊
物料形态
已商用：当前有效
可用性
北美洲, 欧洲
用途
建筑应用领域
加工方式
注射成型
其他属性
填料/增强材料, 添加剂, 特性, 机构评级, 外观, 形式, 密度 / 比重, 密度, 熔融体积流量（MVR）, 收缩率, 吸水率Sat/23C, 吸水率23C/50RH, 拉伸模量, 拉伸屈服应力, 拉伸断裂应力, 拉伸应力, 拉伸屈服应变, 标称拉伸断裂应变, 简支梁缺口冲击强度, 简支梁无缺口冲击强度, DTUL (0.45 MPa) 未退火, DTUL (1.80 MPa) 未退火, 维卡软化温度, 熔融峰值温度, 熔融温度, 线性热膨胀系数，流动, 线热膨胀系数，垂直, 体积电阻率, 介电强度, 相对电容率, 耗散因数, 漏电起痕指数, 可燃性等级, 加工（熔体）温度, 模具温度, 注塑压力
加工
Find specific processing information for VESTAMID® L Polyamide 12 as well as general information for the 聚酰胺 12 generic family. 注册 或 登录 了解更多信息。