VESTAMID® D DX9304 BK E70238
VESTAMID® DX9304 BK E70238 is a PA 612 extrusion compound developed for the manufacturing of tubing systems with higher demands on heat resistance.
The melting point of VESTAMID® DX9304 BK E70238, about 35 °C higher than PA 11 and PA 12 compounds, allows higher temperatures in use. The compound is especially suitable for the extrusion of tubing systems that are exposed to high burst pressures at high service temperatures, e.g. hydraulic clutch lines.
The material absorbs only little moisture. Therefore dimensions and properties of parts are nearly unaffected through ambient conditions.
Pigmentation may affect values.
The melting point of VESTAMID® DX9304 BK E70238, about 35 °C higher than PA 11 and PA 12 compounds, allows higher temperatures in use. The compound is especially suitable for the extrusion of tubing systems that are exposed to high burst pressures at high service temperatures, e.g. hydraulic clutch lines.
The material absorbs only little moisture. Therefore dimensions and properties of parts are nearly unaffected through ambient conditions.
Pigmentation may affect values.
一般属性
使用 Prospector 建立免費帳戶時，可造訪 VESTAMID® D DX9304 BK E70238 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊
物料形态
已商用：当前有效
可用性
北美洲, 欧洲
用途
管道
加工方式
挤出
其他属性
添加剂, 特性, 外观, 形式, 密度 / 比重, 密度, 熔融体积流量（MVR）, 收缩率, 吸水率Sat/23C, 吸水率23C/50RH, 拉伸模量, 拉伸屈服应力, 拉伸断裂应力, 拉伸应力, 拉伸屈服应变, 标称拉伸断裂应变, 弯曲模量, 弯曲应力, 简支梁缺口冲击强度, 简支梁无缺口冲击强度, 肖氏硬度, DTUL (0.45 MPa) 未退火, DTUL (1.80 MPa) 未退火, 维卡软化温度, 熔融峰值温度, 熔融温度, 线性热膨胀系数，流动, 表面电阻率, 体积电阻率, 介电强度, 相对电容率, 耗散因数, 漏电起痕指数, 可燃性等级, 其他性能, 加工（熔体）温度, 模具温度
加工
Find specific processing information for VESTAMID® D Polyamide 612 as well as general information for the 聚酰胺 612 generic family. 注册 或 登录 了解更多信息。
购买地点
您可以從 4 個經銷商或製造商處購買 VESTAMID® D DX9304 BK E70238。 注册 或 登录 了解更多信息。