Texin® 575D
Texin 575D resin is a blend of polyester-based polyurethane and polycarbonate. This aromatic grade has a Shore hardness of approximately 75D*. It can be processed by injection molding or extrusion.
Properties / Applications:
Texin 575D resin offers high impact strength, and high stiffness, as well as excellent low-temperature properties. Typical applications include automotive cladding, fascia, bumpers, and a wide variety of injection molded and extruded articles. As with any product, use of Texin 575D resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
Properties / Applications:
Texin 575D resin offers high impact strength, and high stiffness, as well as excellent low-temperature properties. Typical applications include automotive cladding, fascia, bumpers, and a wide variety of injection molded and extruded articles. As with any product, use of Texin 575D resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
一般属性
使用 Prospector 建立免費帳戶時，可造訪 Texin® 575D 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊
物料形态
已商用：当前有效
文档
可用性
北美洲, 欧洲
用途
汽车防撞杆
加工方式
挤出
其他属性
特性, 密度 / 比重, 密度, 流动方向收缩, 垂直流动方向的收缩, 收缩率, 弯曲模量, 弯曲模量, 泰伯耐磨性, 抗张强度, 拉伸断裂应力, 断裂伸长率, 拉伸断裂应变, 撕裂强度, 撕裂强度, 巴肖氏弹性, 悬壁梁缺口冲击强度, 肖氏硬度, 肖氏硬度, DTUL (66 psi) - 未退火, DTUL (0.45 MPa) 未退火, DTUL (264 psi) - 未退火, DTUL (1.80 MPa) 未退火, 脆化温度, 脆化温度, 玻璃转化温度, 维卡软化温度, 维卡软化温度, CLTE，流动, UL 阻燃等级, 其他性能, 干燥温度, 干燥时间, 建议的最大水分含量, 建议注射量, 建议的最大回制料比例, 料筒后部温度, 料筒中部温度, 料筒前部温度, 射嘴温度, 加工（熔体）温度, 模具温度, 注塑压力, 注射速度, 螺杆转速, 锁模力, 垫层, 螺杆长径比, 螺杆压缩比, 干燥温度, 干燥时间, 建议的最大水分含量, 建议的最大回制料比例, 料筒1区温度, 料筒2区温度, 料筒3区温度, 熔体温度, 口模温度, 螺杆长径比
加工
Find specific processing information for Texin® TPU as well as general information for the 热塑性聚氨酯弹性体（聚碳酸酯基） generic family. 注册 或 登录 了解更多信息。