VESTAMID® L L1930 NC
VESTAMID® L1930 NC is a heat stabilized, with 30% milled glass fiber-reinforced PA 12 compound suitable for injection molding of stiff, relatively warp free molded parts.
Due to the reinforcement moldings from this compound exhibit a high strength and rigidity. Because PA 12 absorbs only little water, the parts have a good dimensional stability and almost unaffected mechanical properties at changing ambient humidity.
Due to the reinforcement the shrinking of moldings is decreased compared with unreinforced compounds. Using specialty short glass fibers for the reinforcement of VESTAMID® L1930 NC the difference between longitudinal and transverse shrinkage relating to the flow direction of the melt is significantly lower than with common glass fiber-reinforced products. Therefore especially low-warpage precision parts can be molded.
As a semi-crystalline material VESTAMID® L1930 NC feature an outstanding chemical resistance, e.g., against fuels, oils and fats.
Pigmentation may affect values.
Due to the reinforcement moldings from this compound exhibit a high strength and rigidity. Because PA 12 absorbs only little water, the parts have a good dimensional stability and almost unaffected mechanical properties at changing ambient humidity.
Due to the reinforcement the shrinking of moldings is decreased compared with unreinforced compounds. Using specialty short glass fibers for the reinforcement of VESTAMID® L1930 NC the difference between longitudinal and transverse shrinkage relating to the flow direction of the melt is significantly lower than with common glass fiber-reinforced products. Therefore especially low-warpage precision parts can be molded.
As a semi-crystalline material VESTAMID® L1930 NC feature an outstanding chemical resistance, e.g., against fuels, oils and fats.
Pigmentation may affect values.
一般的な属性
Prospectorで無料のアカウントを作成し、VESTAMID® L L1930 NCのデータシート詳細すべてにアクセスします。そこで、物理、機械、硬度仕様に関するすべての情報をご覧ください
材料ステータス
供給可能
ドキュメント
description
Processing - Vestamid (English)
ドキュメントのダウンロード可用性
欧州, 北アメリカ
用途
一般用途
加工方法
射出成形
その他の属性
フィラー／強化剤, 添加剤, 特徴, 規格、標準、規制、認可関連, 外観, 形状, 密度 / 比重, 密度, メルトボリュームフローレート（MVR）, 成形収縮, 給水率 平衡/23℃, 吸水率 23℃/50ＲＨ, 引張弾性率, 引張降伏応力, 引張破壊応力, 引張り応力, 引張り降伏歪み, 引張り破壊呼び歪み, シャルピー衝撃強度（ノッチ付）, シャルピー衝撃強度（ノッチなし）, DTUL (0.45 MPa) アニールなし, DTUL (1.80 MPa) アニールなし, ビカット軟化温度, ピーク溶融温度, 溶解温度, 線膨張係数、平行, 線膨張係数、垂直, 体積抵抗率, 耐電圧, 比誘電率, 拡散率, 耐トラッキング性, 燃焼性の区分, 成形（溶融）温度, 金型温度, 射出圧力
加工
VESTAMID® L Polyamide 12の具体的な加工情報や、Polyamide 12ジェネリックファミリーの一般情報をご確認いただけます。 登録 または サインイン 詳細情報を確認してください。
ご購入方法
4の販売業者や製造者からVESTAMID® L L1930 NCを購入できます。 登録 または サインイン 詳細情報を確認してください。
Prospectorのログイン/登録
プレミアム機能
ULイエローカードを検索
ULイエローカードはグローバルに認められている安全認証および品質情報のカードです。プラスチックが特定のパフォーマンス基準をどのように満たしているかを示します。
PROSPECTOR
材料だけでなく、ソリューションも見つけることができます。
Prospectorにご登録いただくと、ダイナミックなツールおよび機能を活用して、迅速にソリューションを見つけることができます。
今すぐご登録ください