LNP™ COLORCOMP™ COMPOUND CQ518811-NC is a GPPS based masterbatch for XPS foaming applications containing a nanostructured, non-mineral based additive. Typical usage levels in final foam formulations are below 5%.

LNP LUBRICOMP CG002XXN compound is based on Polystyrene (PS) resin containing graphite. Added features of this grade include: Wear Resistant.

LNP LUBRICOMP CG006 compound is based on Polystyrene (PS) resin containing graphite. Added features of this grade include: Wear Resistant.

LNP LUBRICOMP CGI11XP compound is based on Polystyrene (PS) resin containing graphite. Added features of this grade include: Wear Resistant.

LNP LUBRICOMP CL002 compound is based on Polystyrene (PS) resin containing 10% PTFE. Added features of this grade include: Wear Resistant.

LNP LUBRICOMP CX94108 compound is based on Polystyrene (PS) resin containing proprietary lubricant. Added features of this grade include: Wear Resistant.

LNP LUBRICOMP CZL36 compound is based on Polystyrene (PS) resin containing 30% milled glass and 15% PTFE. Added features of this grade include: Wear Resistant.

LNP STAT-KON CD000 compound is based on Polystyrene (PS) resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive.

LNP STAT-KON CD000I compound is based on Polystyrene (PS) resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive, High Impact.

LNP STAT-KON CD000I compound is based on Polystyrene (PS) resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive, High Impact.

LNP STAT-KON CX01039 compound is based on Polystyrene (PS) resin containing proprietary fillers. Added features of this grade include: Electrically Conductive.

LNP THERMOCOMP CX05470 compound is based on Polystyrene (PS) resin containing 20% glass fiber.

Fire retardant expanded Polystyrene SABIC® EPS450FF is manufactured by the suspension polymerization of styrene monomer. The polymerization is generally carried out in a batch process. SABIC® EPS450FF is an expandable polystyrene grade supplied in free flowing beads, containing pentane (CFC free) as a foaming agent. It is used for fast cycle shape and block molding applications with good surface finish.

Standard expanded Polystyrene SABIC® EPS452 is manufactured by the suspension polymerization of styrene monomer. The polymerization is generally carried out in a batch process. SABIC® EPS452 is an expandable polystyrene grade supplied in free-flowing beads, containing pentane (CFC free) as a foaming agent. It is used for fast cycle shape and block molding applications with good surface finish.

Fire retardant expanded Polystyrene SABIC® EPS550FF is manufactured by the suspension polymerization of styrene monomer. The polymerization is generally carried out in a batch process and it contains a fire retarding additive in the formulation. SABIC® EPS550FF is an expandable polystyrene grade supplied in free-flowing beads containing pentane (CFC free) as a foaming agent.

Standard expanded Polystyrene SABIC® EPS552 is manufactured by the suspension polymerization of styrene monomer. The polymerization is generally carried out in a batch process. SABIC® EPS552 is supplied in free flowing beads, containing pentane (CFC free) as a foaming agent. It is used for fast cycle low density block molding applications with good surface finish.

Fire retardant expanded Polystyrene SABIC® EPS650FF is manufactured by the suspension polymerization of styrene monomer. The polymerization is generally carried out in a batch process. SABIC® EPS650FF is supplied in free flowing beads, containing pentane (CFC free) as a foaming agent. It is used for fast cycle low density block molding applications with good surface finish.

Standard expanded Polystyrene SABIC® EPS652 is manufactured by the suspension polymerization of styrene monomer. The polymerization is generally carried out in a batch process. SABIC® EPS763 is an expandable polystyrene grade supplied in free flowing beads, containing pentane (CFC free) as a foaming agent. It is used for fast cycle low density block molding applications with good surface finish.

Fire retardant expanded Polystyrene SABIC® EPS760FF is manufactured by the suspension polymerization of styrene monomer. The polymerization is generally carried out in a batch process and it contains a fire retarding additive in the formulation. SABIC® EPS760FF is an expandable polystyrene grade supplied in free-flowing beads containing pentane (CFC free) as a foaming agent.

Standard expanded Polystyrene SABIC® EPS763 is manufactured by the suspension polymerization of styrene monomer. The polymerization is generally carried out in a batch process. SABIC® EPS763 is an expandable polystyrene grade supplied in free-flowing beads, containing pentane (CFC free) as a foaming agent. It is used for fast cycle low density block molding applications with good surface finish.

PS 100 is general purpose Polystyrene manufactured by continuous mass polymerization of styrene monomer. It is a crystal-like, hard and brittle polymer with good flow properties and high clarity. It is designed for medium and thin wall thickness articles and gives broad processing window for molding applications.

125 is general purpose Polystyrene manufactured by continuous mass polymerization of styrene monomer. It is a crystal-like, hard and brittle polymer with medium flow and high clarity. It also has medium vicat and heat deflection temperatures and makes it suitable for various applications.

General purpose Polystyrene PS 155 is manufactured by continuous mass polymerization of styrene monomer. It is a crystal-like, hard and brittle polymer with medium flow and good tensile and flexural strength. It has high vicat and heat deflection temperatures.

General purpose Polystyrene PS 160 is manufactured by continuous mass polymerization of styrene monomer. It is a crystal-like, hard and brittle material having High molecular weight imparting high tensile strength to end- products. It has high vicat and heat deflection temperatures.

PS 325 is High Impact Polystyrene manufactured by continuous mass polymerization of styrene monomer. An elastomer is incorporated during polymerization to achieve impact resistance property. It is generally opaque in color. It is having medium flow characteristics with high tensile and flexural strength with medium heat deflection and vicat temperatures.

PS 330 is high Impact Polystyrene manufactured by continuous mass polymerization of styrene monomer. An elastomer is incorporated during polymerization to achieve impact resistance property. It is generally opaque in color. It is a high impact strength polystyrene with high heat deflection temperature and good physical properties.