AKROMID® T9 GF 30 S1 black (7873) is a 30% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state. Parts with tight dimensional tolerances even under high mechanical load.

AKROMID® T9 GF 35 4 schwarz (7858) is a 35% glass fibre reinforced polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state. Parts with tight dimensional tolerances even under high mechanical load.

AKROMID® T9 GF 40 4 schwarz (7828) is a 40% glass fibre reinforced polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state. Parts with tight dimensional tolerances even under high mechanical load.

AKROMID® T9 GF 50 6 schwarz (7917) is a 50% glass fibre reinforced polyphthalamide with heat stabilization, high rigidity and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state. Parts with tight dimensional tolerances even under high mechanical load.

AKROMID® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state. Parts with tight dimensional tolerances even under high mechanical load.

AKROMID® T9 GF 50 black (7693) is a 50% glass fibre reinforced polyphthalamide with heat stabilization, high rigidity and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state. Parts with tight dimensional tolerances even under high mechanical load.

AKROMID® T9 ICF 20 6 black (7907) is a 20% carbon fibre polyphthalamide with high stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state. Technical parts in the automotive and electric industry

AKROMID® T9 ICF 30 6 black (7908) is a 30% carbon fibre polyphthalamide with high stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state. Technical parts in the automotive and electric industry

AKROMID® T9 ICF 40 6 black (7909) is a 40% carbon fibre polyphthalamide with high stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state. Technical parts in the automotive and electric industry

AKROMID® T9 M 40 black (7851) is a 40% mineral-filled polyphthalamide with very good surface and slight tendency to warp, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state. Technical parts in the automotive and electric industry