(PC+ABS)-Blend; 5 % mineral filled; flame retardant; Vicat/B 120 temperature = 103°C; HDT/A >= 85°C; for thin-wall applications; very good UL recognition in small wall thicknesses (V-0 at 0.75 mm); low smoke density

(PC+ABS)-Blend; 15 % mineral filled; with 30 % post consumer recyclate - water bottle content; flame retardant; Vicat/B 120 temperature = 97°C; increased stiffness; tensile modulus = 4600 MPa; UL recognition 94 V-0 at 1.5 mm

(PC+ABS)-Blend; 15 % mineral filled; with 30 % post consumer recyclate; Vicat/B 120 temperature = 98 °C; medium viscosity; medium modulus; low warpage; flame-retardant

(PC+ABS)-Blend; 15 % mineral filled; flame retardant; Vicat/B 120 temperature = 98°C; high stiffness; tensile modulus = 4800 MPa;; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm Partially bio-circular grade / Attributed via mass balance (according to ISCC PLUS Standard).

(PC+ABS)-Blend; 15 % mineral filled; flame retardant; Vicat/B 120 temperature = 98°C; high stiffness; tensile modulus = 4800 MPa;; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm

(PC+ABS)-Blend; flame retardant; mineral filled ; containing 35% post-consumer PC recyclate; Vicat/B 120 temperature = 102°C; UL recognition 94 V-0 at 1.2 mm; low warpage; improved stiffness and surface quality; for notebooks and thinwall applications Partially bio-circular grade / Attributed via mass balance (according to ISCC PLUS Standard).

(PC+ABS)-Blend; flame retardant; mineral filled ; containing 35% post-consumer PC recyclate; Vicat/B 120 temperature = 102°C; UL recognition 94 V-0 at 1.2 mm; low warpage; improved stiffness and surface quality; for notebooks and thinwall applications

(PC+ABS)-Blend; flame retardant; mineral filled ; Vicat/B 120 temperature = 102°C; UL recognition 94 V-0 at 1.2 mm; low warpage; improved stiffness and surface quality; for notebooks and thinwall applications

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 115°C; extrusion grade; good extrusion and vacuum-forming behaviour; UL recognition 94 V-0 at 1.5 mm; halogen-free according to DIN VDE 0472,815; glow wire temperature (GWFI): 960°C at 1.0 mm

(PC+ABS)-Blend; flame retardant; low viscocity; non-reinforced; impact modified; Easy flow; Vicat/B 120 temperature = 108 °C; Housing; for: information technology; Electrical/electronic

(PC+ABS)-Blend; flame retardant; good UV/light transmission (e 380 nm) at low wall thicknesses for UV/light curing adhesives; for thin-wall applications; UL recognition 94 V-0 (1.0 mm); only natural color (000000) available; for thin-wall applications

containing 35% post-consumer PC recyclate; flame retardant; injection molding grade; for notebooks and thinwall applications

containing 35% post-consumer PC recyclate; flame retardant; injection molding grade; for notebooks and thinwall applications

PC+ABS-FR(40)-Blend; flame retardant; for notebooks and thinwall applications Partially bio-circular grade / Attributed via mass balance (according to ISCC PLUS Standard).

PC+ABS-FR(40)-Blend; flame retardant; for notebooks and thinwall applications

PC+ABS-FR(40)-Blend; flame retardant; for thin-wall applications; only black color (901510) available

(PC+ABS)-Blend; flame retardant; high heat resistant injection molding grade; improved chemical resistance and stress cracking behavior compared to KU2-1514; Vicat/B 120 temperature = 136°C; ball indentation temperature >= 125°C; UL recognition 94 V-1 at 1.0 mm; suitable as supporting material for energized parts

(PC+ABS)-Blend; 15% glass fibre reinforced; flame retardant; Vicat/B 120 temperature = 100 °C; UL recognition 94 V-0 at 1.5 mm and 5VA at 2 mm

(PC+ABS)-Blend; flame retardant; easy flowing; Vicat/B 120 temperature = 110°C; increased heat resistance; UL recognition 94 V-0 at 1.5 mm

(PC+ABS)-Blend; flame retardant; easy flowing; Vicat/B 120 temperature = 93°C; improved surface quality; UL recognition 94 V-0 at 1.2 mm

(PC+ABS)-Blend; 15% glass fibre reinforced; flame retardant; easy flowing; Vicat/B 120 temperature = 96°C; UL recognition 94 V-1 at 1.2 mm and V-0 at 1.5 mm

Rubber modified PC blend; flame retardant; mineral filled ; Vicat/B 120 temperature = 99°C; extrusion grade for European railway interiors requiring EN45545; the classifications according to the respective rail standards are communicated with email inquiry under plastics@covestro.com

(PC+ABS)-Blend; flame retardant; with 30 % post consumer recyclate; Vicat/B 120 temperature = 108°C; UL recognition 94 V-0 at 1.5 mm

(PC+ABS)-Blend; Vicat/B 120 = 105°C; suitable for use in electrical and electronic devices; Manufactured according to GMP; tested only according to ISO 10993-5 and ISO 10993-10 for contact with uncompromised skin only; for questions regarding biocompatibility we ask for an email inquiry under plastics@covestro.com

(PC+ABS)-Blend; Vicat/B 120 temperature = 115°C; suitable for use in electrical and electronic devices; Manufactured according to GMP; tested only according to ISO 10993-5 and ISO 10993-10 for contact with uncompromised skin only; for questions regarding biocompatibility we ask for an email inquiry under plastics@covestro.com

(PC+ABS)-Blend; Vicat/B 120 temperature = 126°C; meet certain requirements of ISO Standard 10993-1; for further information please contact plastics@covestro.com

(PC+ABS)-Blend; easy flowing; Vicat/B 120 temperature = 131°C; meet certain requirements of ISO Standard 10993-1; for further information please contact plastics@covestro.com

(PC+ABS)-Blend; suitable for use in electrical and electronic devices; Easy flow; injection molding grade

ABS+PC-Blend; Vicat/B 120 temperature = 112 °C; easy flowing; improved UV resistance

ABS+PC-Blend; Vicat/B 120 temperature = 112°C; for electroplating applications

formely Bayblend® TP2350; ABS+PC-Blend; Vicat/B 120 temperature = 113°C; for electroplating applications

(PC+ABS)-Blend; Vicat/B 120 temperature = 112°C; excellent flow; good low temperature impact strength

(PC+ABS)-Blend; Vicat/B 120 temperature = 121°C; improved antistatic behavior

(PC+ABS)-Blend; Vicat/B 120 temperature = 120°C; grade with improved low-temperature impact strength and chemical resistance for automotive parts; also suitable for extrusion/extrusion blow molding and electroplating applications

(PC+ABS)-Blend; Vicat/B 120 temperature = 120°C; easy flowing; good heat resistance; for electroplating applications

(PC+ABS)-Blend; Vicat/B 120 temperature = 120°C; improved flow compared with T65

(PC+ABS)-Blend; General Purpose Grade; Vicat/B 120 temperature = 124 °C; good injection molding processing behaviour (easy flowing); excellent long-term ageing behaviour under humid conditions; good painting performance; improved chemical resistance; low VOC emissions and odour

(PC+ABS)-Blend; General Purpose Grade; Vicat/B 120 temperature = 124 °C; good injection molding processing behaviour (easy flowing); excellent long-term ageing behaviour under humid conditions; good painting performance; improved chemical resistance; low VOC emissions and odour

(PC+ABS)-Blend; Vicat/B 120 temperature = 130°C; excellent flow; optimized surface quality for metallization (steam treatment)

(PC+ABS)-Blend; Vicat/B 120 temperature = 130°C; easy flowing; high gloss; brilliant colors