SUMIKASUPER® E6205L
SUMIKASUPER E6205L is a Liquid Crystal Polymer (LCP) product filled with glass fiber/inorganic. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding.
E6000 series which is general-purpose grades are distinguished by their high heat resistance and strength, good moldability and ability to hold tight tolerances, low mold shrinkage, and good mold release. E6000 Series grades are typically processed at 360°C.
E6205L is a 25% glass fiber/inorganic filler grade with low thermal conductivity, low relative permittivity, high lubricity and low friction. E6205L is used for injection molding high-frequency connectors, relay parts, coil seals, bobbins, and office equipment and printer parts.
E6000 series which is general-purpose grades are distinguished by their high heat resistance and strength, good moldability and ability to hold tight tolerances, low mold shrinkage, and good mold release. E6000 Series grades are typically processed at 360°C.
E6205L is a 25% glass fiber/inorganic filler grade with low thermal conductivity, low relative permittivity, high lubricity and low friction. E6205L is used for injection molding high-frequency connectors, relay parts, coil seals, bobbins, and office equipment and printer parts.
一般属性
使用 Prospector 建立免費帳戶時，可造訪 SUMIKASUPER® E6205L 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊
物料形态
已商用：当前有效
文档
description
Contact Information (English)
下载文档
description
Technical Datasheet (Chinese)
下载文档
layers
檢視超過 2 個文件
Download More Documents可用性
北美洲, 拉丁美洲, 欧洲, 亚太地区
用途
电气/电子应用领域
加工方式
注射成型
其他属性
填料/增强材料, 特性, UL文件号, 外观, 形式, 部件标识代码, 密度 / 比重, 密度, 流动方向收缩, 垂直流动方向的收缩, 24小时吸水率, 拉伸模量, 抗张强度, 拉伸应力, 断裂伸长率, 拉伸断裂应变, 弯曲模量, 弯曲模量, 弯曲强度, 弯曲应力, 简支梁无缺口冲击强度, 无缺口悬臂梁冲击, 无缺口伊佐德冲击强度, 洛氏硬度, DTUL (0.45 MPa) 未退火, DTUL (264 psi) - 未退火, DTUL (1.80 MPa) 未退火, 线性热膨胀系数，流动, 线热膨胀系数，垂直, 体积电阻率, 相对电容率, 耗散因数, 可燃性等级, 干燥温度, 干燥时间, 料筒后部温度, 料筒中部温度, 料筒前部温度, 射嘴温度, 加工（熔体）温度, 模具温度, 注塑压力, 保压, 背压, 螺杆转速
加工
Find specific processing information for SUMIKASUPER® as well as general information for the 液晶聚合物 generic family. 注册 或 登录 了解更多信息。